304 stainless coil pipe or stainless steel U pipe
Grade | C% |
Si% |
Mn% |
P% |
S% |
Cr% |
Ni% |
Mo% |
Cu% |
304 |
≤0.08 |
≤1.0 |
≤2.0 |
≤0.045 |
≤0.03 |
18.0-20.0 |
8.0-10.0 |
- |
-- |
T*S |
Y*S |
Hardness |
Elongation |
|
(Mpa) |
(Mpa) |
HRB |
HB |
(%) |
≥520 |
≥205 |
-- |
-- |
≥40 |
Specifications of stainless steel coil pipe:
Grade |
TP304/304L, 316/316L, 310S, 317L, 321, 347H etc (300 series are the main products, if you have special material requirements, please tell us) |
Standard |
ASTM A 213,ASTM A 269,EN10216-5 |
Size |
OD:4.76-25.4mm |
WT:0.71-2.11mm | |
Length:>1000Meters | |
4.76*0.71mm/4.76*0.89mm/4.76*1.24mm | |
6*1mm/6*1.5mm | |
6.35*0.71mm/6.35*0.89mm/6.35*1.24mm/6.35*1.65mm | |
7.94*0.71mm/7.94*0.89mm/7.94*1.24mm/7.94*1.65mm | |
9.53*0.71mm/9.53*0.89mm/9.53*1.24mm/9.43*1.65mm | |
10*1mm/10*1.5mm | |
12*1mm/12*1.5mm/12*2mm | |
12.7*0.71mm/12.7*0.89mm/12.7*1.24mm/12.7*1.65mm/12.7*2.11mm | |
14*1mm/14*1.5mm/14*2mm | |
15.88*0.89mm/15.88*1.24mm/15.88*1.65mm/15.88*2.11mm | |
16*1mm/16*1.5mm/16*2mm | |
19.05*0.89mm/19.05*1.24mm/19.05*1.65mm/19.05*2.11mm | |
25.4*0.89mm/25.4*1.24mm/25.4*1.65mm/25.4*2.11mm |
Stainless steel coil pipe |
Outer diameter :>500mm |
The inner diameter:<1000mm |
|
The height of the coil pipe |
200mm-400mm |
The length of each coil |
Max length:<1000M |
Min length: >6m |
|
General delivery length |
200m-800m |
Physical properties of bright-annealed coil pipe |
A. ratio of elongation no less than 55% |
B. surface hardness no greater 170HV |
|
C. tensile strength no less than 550N/MM2 |
|
D. yield strength no less than 220N/MM2 |
|
E. bending angle>1800;min.bending radius<1.5*pipe diameter |
|
Physical properties of general coil pipe (without bright annealing) |
A. ratio of elongation no less than 35% |
B. surface hardness greater than 180HV |
|
C. tensile strength>600N/MM2 |
|
D. yield strength>280N/MM2 |
|
E. bending angle>900; bending radius>2*pipe diameter |
|
Pressure resistance property |
Take 8*0.5*c coil pipe as an example, the work pressure to be borne by the inner wall is no less than 60BAR |
More details of stainless steel coil pipe:
Type |
Grade |
Grade |
Chemical Component % |
||||||||||
C |
Cr |
Ni |
Mn |
P |
S |
Mo |
Si |
Cu |
N |
Other |
|||
Austenitic stainless steel |
201 |
1Cr17Mn6Ni5N |
≤0.15 |
16.00-18.00 |
3.50-5.50 |
5.50-7.50 |
≤0.060 |
≤0.030 |
- |
≤1.00 |
- |
≤0.25 |
- |
201L |
03Cr17Mn6Ni5N |
≤0.030 |
16.00-18.00 |
3.50-5.50 |
5.50-7.50 |
≤0.060 |
≤0.030 |
≤1.00 |
≤0.25 |
||||
202 |
1Cr18Mn8Ni5N |
≤0.15 |
17.00-19.00 |
4.00-6.00 |
7.50-10.00 |
≤0.060 |
≤0.030 |
≤1.00 |
- |
≤0.25 |
- |
||
204 |
03Cr16Mn8Ni2N |
≤0.030 |
15.00-17.00 |
1.50-3.50 |
7.00-9.00 |
0.15-0.30 |
|||||||
1Cr18Mn10Ni5Mo3N |
≤0.10 |
17.00-19.00 |
4.00-6.00 |
8.50-12.00 |
2.80-3.50 |
0.20-0.30 |
|||||||
2Cr13Mn9Ni4 |
0.15-0.25 |
12.00-14.00 |
3.70-5.00 |
8.00-10.00 |
|||||||||
2Cr15Mn15Ni2N |
0.15-0.25 |
14.00-16.00 |
1.50-3.00 |
14.00-16.00 |
0.15-0.30 |
||||||||
1Cr18Mn10Ni5Mo3N |
≤0.15 |
17.00-19.00 |
4.00-6.00 |
8.50-12.00 |
≤0.060 |
≤0.030 |
2.8-3.5 |
≤1.00 |
- |
0.20-0.30 |
- |
||
301 |
1Cr17Ni7 |
≤0.15 |
16.00-18.00 |
6.00-8.00 |
≤2.00 |
≤0.065 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
302 |
1Cr18Ni9 |
≤0.15 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
303 |
Y1Cr18Ni9 |
≤0.15 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
≤0.20 |
≤0.030 |
1) |
≤1.00 |
- |
- |
- |
|
303se |
Y1Cr18Ni9Se |
≤0.15 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
≤0.20 |
≤0.030 |
- |
≤1.00 |
- |
- |
Se≥0.15 |
|
304 |
0Cr18Ni9 |
≤0.07 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
304L |
00Cr19Ni10 |
≤0.030 |
18.00-20.00 |
8.00-10.00 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
304N1 |
0Cr19Ni9N |
≤0.08 |
18.00-20.00 |
7.00-10.50 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
0.10-0.25 |
- |
|
304N2 |
0Cr18Ni10NbN |
≤0.08 |
18.00-20.00 |
7.50-10.50 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
0.15-0.30 |
Nb≤0.15 |
|
304LN |
00Cr18Ni10N |
≤0.030 |
17.00-19.00 |
8.50-11.50 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
0.12-0.22 |
- |
|
305 |
1Cr18Ni12 |
≤0.12 |
17.00-19.00 |
10.50-13.00 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
309S |
0Cr23Ni13 |
≤0.08 |
22.00-24.00 |
12.00-15.00 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
310S |
0Cr25Ni20 |
≤0.08 |
24.00-26.00 |
19.00-22.00 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
316 |
0Cr17Ni12Mo2 |
≤0.08 |
16.00-18.50 |
10.00-14.00 |
≤2.00 |
≤0.035 |
≤0.030 |
2.00-3.00 |
≤1.00 |
- |
- |
- |
|
1Cr18Ni12Mo2Ti6) |
≤0.12 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
≤0.035 |
≤0.030 |
1.80-2.50 |
≤1.00 |
- |
- |
Ti5(C%-0.02)~0.08 |
||
0Cr18Ni12Mo2Ti |
≤0.08 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
≤0.035 |
≤0.030 |
1.80-2.50 |
≤1.00 |
- |
- |
Ti5*C%-0.70 |
||
316L |
00Cr17Ni14Mo2 |
≤0.030 |
16.00-18.00 |
12.00-15.00 |
≤2.00 |
≤0.035 |
≤0.030 |
2.00-3.00 |
≤1.00 |
- |
- |
- |
|
316N |
0Cr17Ni12Mo2N |
≤0.08 |
16.00-18.00 |
10.00-14.00 |
≤2.00 |
≤0.035 |
≤0.030 |
2.00-3.00 |
≤1.00 |
- |
0.10-0.22 |
- |
|
316N |
00Cr17Ni13Mo2N |
≤0.030 |
16.00-18.50 |
10.50-14.50 |
≤2.00 |
≤0.035 |
≤0.030 |
2.00-3.00 |
≤1.00 |
- |
0.12-0.22 |
- |
|
316J1 |
0Cr18Ni12Mo2Cu2 |
≤0.08 |
17.00-19.00 |
10.00-14.50 |
≤2.00 |
≤0.035 |
≤0.030 |
1.20-2.75 |
≤1.00 |
1.00-2.50 |
- |
- |
|
316J1L |
00Cr18Ni14Mo2Cu2 |
≤0.030 |
17.00-19.00 |
12.00-16.00 |
≤2.00 |
≤0.035 |
≤0.030 |
1.20-2.75 |
≤1.00 |
1.00-2.50 |
- |
- |
|
317 |
0Cr19Ni13Mo3 |
≤0.12 |
18.00-20.00 |
11.00-15.00 |
≤2.00 |
≤0.035 |
≤0.030 |
3.00-4.00 |
≤1.00 |
- |
- |
- |
|
317L |
00Cr19Ni13Mo3 |
≤0.08 |
18.00-20.00 |
11.00-15.00 |
≤2.00 |
≤0.035 |
≤0.030 |
3.00-4.00 |
≤1.00 |
- |
- |
- |
|
1Cr18Ni12Mo3Ti6 |
≤0.12 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
≤0.035 |
≤0.030 |
2.50-3.50 |
≤1.00 |
- |
- |
Ti5(C%-0.02)~0.08 |
||
0Cr18Ni12Mo3Ti |
≤0.08 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
≤0.035 |
≤0.030 |
2.50-3.50 |
≤1.00 |
- |
- |
Ti5*C%-0.70 |
||
317J1 |
0Cr18Ni16Mo5 |
≤0.040 |
16.00-19.00 |
15.00-17.00 |
≤2.00 |
≤0.035 |
≤0.030 |
4.00-6.00 |
≤1.00 |
- |
- |
- |
321 |
1Cr18Ni9Ti6 |
≤0.12 |
17.00-19.00 |
8.00-11.00 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
Ti5(C%-0.02)~0.08 |
|
0Cr18Ni10Ti |
≤0.08 |
17.00-19.00 |
9.00-12.00 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
Ti≥5*C% |
||
347 |
0Cr18Ni11Nb |
≤0.08 |
17.00-19.00 |
9.00-13.00 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
Nb≥10*C% |
|
XM7 |
0Cr18Ni9Cu3 |
≤0.08 |
17.00-19.00 |
8.50-10.50 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
3.00-4.00 |
- |
- |
|
XM15J1 |
0Cr18Ni13Si4 |
≤0.08 |
15.00-20.00 |
11.50-15.00 |
≤2.00 |
≤0.035 |
≤0.030 |
- |
3.00-5.00 |
- |
- |
2) |
|
Austenite |
329J1 |
0Cr26Ni5Mo2 |
≤0.08 |
23.00-28.00 |
3.00-6.00 |
≤1.50 |
≤0.035 |
≤0.030 |
1.00-3.00 |
≤1.00 |
- |
- |
2) |
1Cr18Ni11Si4AlTi |
0.10-0.18 |
17.50-19.50 |
10.--120.. |
≤0.80 |
≤0.035 |
≤0.030 |
- |
3.40-4.00 |
- |
- |
Al 0.10-0.30; Ti 0.40-0.70 |
||
00Cr18Ni5MoSi2 |
≤0.030 |
18.00-19.50 |
4.50-5.50 |
1.00-2.00 |
≤0.035 |
≤0.030 |
2.50-3.00 |
1.30-2.00 |
- |
- |
- |
||
Ferrite Stainless Steel |
405 |
0Cr13Al |
≤0.08 |
11.50-14.50 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
Al 0.10-0.30 |
410L |
00Cr12 |
≤0.030 |
11.00-13.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
430 |
1Cr17 |
≤0.12 |
16.00-18.00 |
3) |
≤1.25 |
≤0.035 |
≤0.030 |
- |
≤0.75 |
- |
- |
- |
|
430F |
Y1Cr17 |
≤0.12 |
16.00-18.00 |
3) |
≤1.00 |
≤0.035 |
≥0.15 |
1) |
≤1.00 |
- |
- |
- |
|
434 |
1Cr17Mo |
≤0.12 |
16.00-18.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
0.75-1.25 |
≤1.00 |
- |
- |
- |
|
447J1 |
00Cr30Mo2 |
≤0.010 |
28.50-32.00 |
- |
≤0.40 |
≤0.035 |
≤0.030 |
1.50-2.50 |
≤0.40 |
- |
≤0.015 |
- |
|
XM27 |
00Cr27Mo |
≤0.010 |
25.00-27.50 |
- |
≤0.40 |
≤0.035 |
≤0.030 |
0.75-1.50 |
≤0.40 |
- |
≤0.015 |
- |
|
Martensite stainless steel |
403 |
1Cr12 |
≤0.15 |
11.50-13.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤0.50 |
- |
- |
- |
410 |
1Cr13 |
≤0.15 |
11.50-13.50 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
405 |
0Cr13 |
≤0.08 |
11.50-13.50 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
416 |
Y1Cr13 |
≤0.15 |
12.00-14.00 |
3) |
≤1.25 |
≤0.035 |
≥0.15 |
1) |
≤1.00 |
- |
- |
- |
|
410J1 |
1Cr13Mo |
≤0.08-0.18 |
11.50-14.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
0.30-0.60 |
≤0.60 |
- |
- |
- |
|
420J1 |
2Cr13 |
0.16-0.25 |
12.00-14.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
420J2 |
3Cr13 |
0.26-0.35 |
12.00-14.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
|
420F |
Y3Cr13 |
0.26-0.40 |
12.00-14.00 |
3) |
≤1.25 |
≤0.035 |
≥0.15 |
1) |
≤1.00 |
- |
- |
- |
|
3Cr13Mo |
0.28-0.35 |
12.00-14.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
0.50-1.00 |
≤0.80 |
- |
- |
- |
||
4Cr13 |
0.36-0.45 |
12.00-14.00 |
3) |
≤0.80 |
≤0.035 |
≤0.030 |
- |
≤0.60 |
- |
- |
- |
431 |
1Cr17Ni2 |
0.11-0.17 |
16.00-18.00 |
1.50-2.50 |
≤0.80 |
≤0.035 |
≤0.030 |
- |
≤0.80 |
- |
- |
- |
|
440A |
7Cr17 |
0.60-0.75 |
16.00-18.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
4) |
≤1.00 |
- |
- |
- |
|
440B |
8Cr17 |
0.75-0.95 |
16.00-18.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
4) |
≤1.00 |
- |
- |
- |
|
9Cr18 |
0.90-1.00 |
17.00-19.00 |
3) |
≤0.80 |
≤0.035 |
≤0.030 |
4) |
≤0.80 |
- |
- |
- |
||
440C |
11Cr17 |
0.95-1.20 |
16.00-18.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
4) |
≤1.00 |
- |
- |
- |
|
440F |
Y11Cr17 |
0.95-1.20 |
16.00-18.00 |
3) |
≤1.25 |
≤0.035 |
≥0.15 |
4) |
≤1.00 |
- |
- |
- |
|
9Cr18Mo |
0.95-1.10 |
16.00-18.00 |
3) |
≤0.80 |
≤0.035 |
≤0.030 |
0.40-0.70 |
≤0.80 |
- |
- |
- |
||
9Cr18MoV |
0.85-0.95 |
17.00-19.00 |
3) |
≤0.80 |
≤0.035 |
≤0.030 |
1.00-1.30 |
≤0.80 |
- |
- |
V0.07-0.12 |
||
PH Stainless Steel |
630 |
0Cr17Ni4Cu4Nb |
≤0.07 |
15.50-17.50 |
6.50-7.50 |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
3.00-5.00 |
- |
Nb 0.15-0.45 |
631 |
0Cr17Ni7Al |
≤0.09 |
16.00-18.00 |
6.50-7.50 |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
≤0.50 |
- |
Al 0.75-1.50 |
|
632 |
0Cr15Ni7Mo2Al |
≤0.09 |
14.00-16.00 |
6.50-7.50 |
≤1.00 |
≤0.035 |
≤0.030 |
2.00-3.00 |
≤1.00 |
- |
- |
Al 0.75-1.50 |
SASA METAL, established in 1995, is an experienced and professional manufacturers and suppliers of stainless steel coil pipe. With the aid of qualified workers and advanced equipment, we can assure you the high quality and good performance of our products. Please be free to buy products for sale with us.